NACERA® PEARL MULTI-SHADE.

Passion for Beautiful Teeth
New
Multi-Layered Zirconia
NACERA PEARL MULTI-SHADE.
®
THE ERGONOMIC SYSTEM FOR NATURAL-LOOKING
RESTORATIONS.
THIS IS HOW YOU BENEFIT FROM OUR
PASSION FOR BEAUTIFUL TEETH:
WE HAVE DEVELOPED AN ERGONOMIC
MULTI-LAYERED SYSTEM MADE OF HIGHLY
TRANSLUCENT ZIRCONIUM DIOXIDE.
Mit Nacera Pearl Multi-Shade guarantees smooth,
invisible transitions within the restoration.
®
We offer a new version of our best material: Nacera® Pearl Multi-Shade
zirconium dioxide. After sintering, Multi-Shade blanks replicate the smooth
transition of colors you can observe in real teeth, thereby full contour as
well as substructures constructions with a natural appearance.
To achieve most common tooth colors, Nacera® Pearl Multi-Shade blanks
are available in the Vita shades A, B, C, and D. Their application is quite
simple: Depending on the height positioning, for example, the colors A3, A2
or A1 can be attained in an A-blank. The same is true for the other shades.
The structural height of 18 mm ensures that sufficient space for vertical
shifting is available.
Thus, you receive an efficient and ergonomic multi-layered system, which
covers almost all Vita classic shades with only four different blanks.
Finished with a stain-and-glazing technique or using minimal stratification by Cut-Back, Nacera® Pearl is always a reliable quality foundation for
monolithic constructions, that meet the highest requirements for natural
esthetics.
A1
A2
Vita A2
Multi-Shade C
Top
Vita C1
Multi-Shade C
Middle
Vita C2
Multi-Shade A
Bottom
Vita A3
Multi-Shade C
Bottom
Vita C3
Multi-Shade B
Top
Vita B1
Multi-Shade D
Top
Vita D1
Multi-Shade B
Middle
Vita B2
Multi-Shade D
Middle
Vita D2
Multi-Shade B
Bottom
Vita B3
Multi-Shade D
Bottom
Vita D3
Benefits & Indication
Physical properties* Nacera Pearl Multi-Shade
®
Material
Highly translucent multi-layered system
Natural and smooth transitions from cervical to incisal
Extremely efficient: one blank covers three shades
Quick and economical for natural-looking monolithic restorations
Flexural strength (biaxial): 1400 MPa
Excellent Machinability: Thin margins can be milled without having to worry about chipping or cracks. Lifetime of milling burs increases up to 15 %
Color
Density
ZrO2 Y-TZP
weiß transluzent
> 6,04 g/cm3
Flexural strength (biaxial)
1400 MPa
Compressive strength
3000 MPA
Modulus of elasticity
205 GPa
Impact Resistance
8 MPa m1/2
Vickers Hardness
1300 HV 0,5
Thermal expansion
10 10-6 k-1
Thermal conductivity
2 W/mK
Mean linear intercept
< 0,4 mm
Radioactivity
< 0,02 Bq/g
Solubility
< 10 mg/cm2
Composition
All Nacera® zirconia products hold a marketability according to 93/42 EEC.
The notified body is TÜV-SÜD (CE 0123).
18 mm
Vita A1
Middle
18 mm
Top
Multi-Shade A
18 mm
Multi-Shade A
18 mm
A3
ZrO2 + HfO2 + Y2O3 > 99%, Y2O3 4,5% - 6%
*These properties were measured on test samples. The values are typical material properties
and may vary according to product configuration, geometry and manufacturing process.
Passion for Beautiful Teeth
Our selection: Premium zirconium dioxide
for CAD/CAM systems
Do you have any questions regarding our products?
Call
+49 231. 9256 68-0
www.nacera.de/en
Your Nacera® distributor:
For an overview of all global representations
go to: www.nacera.de/en
Nacera products are approved for:
®
Europe | USA | Canada | Mexico | Brazil | Australia | China
DOCERAM Medical Ceramics GmbH
Hesslingsweg 65 - 67 | 44309 Dortmund | Germany
Phone +49 231. 9256 680 | [email protected] | www.nacera.de/en
A member of the
MOESCHTER GROUP