Shalilac Deck Finish - Shalimar Paints Industrial Business

MARINEGUARD
PROTECTIVE COATINGS
SHALILAC DECK FINISH
A durable, weather-resistant coating based on Synthetic resin medium for the protection of Steel Decks. Designed
to withstand the rough usages at sea and port. This is a type of conventional deck coating which combines ease of
application with toughness, abrasion resistance and durability.
Product Information
Colour
Selected range
Finish
Glossy
Flash Point
Above 30˚C
Mixing Ratio
Base : Accelerator 1 : 1
Solid Volume
36% approx.
Recommended
dry film thickness
30 - 35 microns per coat
Corresponding wet
film thickness
83 - 97 microns per coat
Theoretical
Spreading Rate
12.0 – 10.3 Sq.metre per litre
Coverage
with loss factor 20%
with loss factor 30%
with loss factor 40%
9.6 - 8.2 sq. metre/ltr./coat
8.4 - 7.2 sq. metre/ltr./coat
7.2 - 6.8 sq. metre/ltr./coat
Surface Preparation
STEEL SURFACES:
All surface should be clean, dry, free from oil and
grease and primed with Shaliprime Orange/
Yellow/Red.
Application Details
Drying time
Surface dry - 4 hours
Hard dry
- 8 - 12 hours
Method of Application:
Brush / Spray / Roller
Airless spray recommended for uniform and high
film build.
Interval before
Overcoating
18 hours minimum, No maximum
Notes on Airless Spray:
Dry Heat Resistance
Upto 150˚C (intermittent)
Total output fluid pressure
2500 - 3000 psi.
(176 - 211 kg/sq. cm.)
Storage life
1 Year
Thinner:
Tip Ranger -
21 - 26 thou.
MTH 002
Shalimar Paints Ltd.: 4th Floor, Plot No. 64, Sector-44
Gurgaon -122001, Haryana (India) | P: +91-124-4616600 | F: +91-124-4616659
E: [email protected] | www.shalimarpaints.com
DISCLAIMER: The information in this leaflet is given in good faith. The company will not be liable for loss or damage howsoever caused
including liability for negligence, which may be suffered by the user of the data contained therein. It is the user's responsibility to conduct
all necessary tests to confirm the suitability of any product or system for their intended use. No guarantee of result is extended since
conditions of use are beyond our control.
1